UT-ML Zirconia Block
UT-ML Zirconia Block
Proprietà di base
Paese Di Origine
Cina
Marchio
APPLEDENTAL
Certificato
MDR、CE、ISO、FDA
Modello Di Prodotto
UT-ML
Proprietà Commerciali
Riepilogo Prodotto
Model:UT-ML Extremely transparent multilayer ·Extreme Translucency·Natural Gradient·Easy Workflow·Anterior-focused Multi-layered gradient structure design, with natural and soft color transitions, no need for additional staining, simplifying the processing workflow; High translucency texture formula...
Dettagli del prodotto
Density Before Sintering(G·Cm⁻³):
≥3.0
Density After Sintering(G·Cm⁻³):
6,07±0,02
Coefficient Of Thermal Expansion(25-500℃) (K⁻¹):
10,4±0,5
Bending Strength After Sintering (MPa):
500-650
Transparency(1.0±0.02 Mm):
46%-49%
Chemical Solubility After Sintering(Μg·Cm⁻²):
<100
Cytotoxicity:
Livello 0
Radioactivity(Bq·G⁻¹):
< 0.1
Fracture Toughness:
5,0 MPa·m¹ᐟ²
Accelerated Aging Surface Monoclinic Phase Content:
<15%
Sintering Temperature(℃):
1450
Descrizione di prodotto
Model:UT-ML Extremely transparent multilayer ·Extreme Translucency·Natural Gradient·Easy Workflow·Anterior-focused Multi-layered gradient structure design, with natural and soft color transitions, no need for additional staining, simplifying the processing workflow; High translucency texture formula, transparency 46%-49%, restoring natural tooth luster, the core choice for anterior aesthetic restorations; Bending strength 500-650MPa, suitable for anterior veneers, inlays