UT-ML Zirconia Block
UT-ML Zirconia Block
Propriétés de base
Pays D'Origine
Chine
Nom De La Marque
APPLEDENTAL
Certificat
MDR、CE、ISO、FDA
Modèle De Produit
UT-ML
Propriétés commerciales
Résumé du produit
Model:UT-ML Extremely transparent multilayer ·Extreme Translucency·Natural Gradient·Easy Workflow·Anterior-focused Multi-layered gradient structure design, with natural and soft color transitions, no need for additional staining, simplifying the processing workflow; High translucency texture formula...
Détails du produit
Density Before Sintering(G·Cm⁻³):
≥3.0
Density After Sintering(G·Cm⁻³):
6,07 ± 0,02
Coefficient Of Thermal Expansion(25-500℃) (K⁻¹):
10,4 ± 0,5
Bending Strength After Sintering (MPa):
500-650
Transparency(1.0±0.02 Mm):
46% à 49%
Chemical Solubility After Sintering(Μg·Cm⁻²):
<100
Cytotoxicity:
0 Niveau
Radioactivity(Bq·G⁻¹):
Le taux de dépôt1
Fracture Toughness:
5,0 MPa·m¹ᐟ²
Accelerated Aging Surface Monoclinic Phase Content:
<15%
Sintering Temperature(℃):
1450
Description de produit
Model:UT-ML Extremely transparent multilayer ·Extreme Translucency·Natural Gradient·Easy Workflow·Anterior-focused Multi-layered gradient structure design, with natural and soft color transitions, no need for additional staining, simplifying the processing workflow; High translucency texture formula, transparency 46%-49%, restoring natural tooth luster, the core choice for anterior aesthetic restorations; Bending strength 500-650MPa, suitable for anterior veneers, inlays